附件 13 版本号 :FH-2013-001 风华高科 X8R 多层片状陶瓷电容器 一 概述 电容器及介质种类 : X8R: 此类介质材料的电容器为 Ⅱ 类电容器, 具有较高的介电常数, 具有高达 150 的上限使用温度和稳定的温度特性, 可靠性高, 可应用于高温环境中的各种电子设备中, 如汽车电子, 石油勘探设备及照明电子等 X8R MLCC SUMMARY Types of Dielectric Material and Capacitor X8R: The capacitor made from X8R material is considered as Class Ⅱ capacitor with high dielectric constant. These capacitors can be used for applications up to 150 with stable performance and high reliability. These capacitors are fit for applications exposed to high temperature such as automotive electronics, oil exploration equipments and lighting equipments, etc. 第 1 页共 13 页
二 尺寸及结构 DIMENSIONS AND STRUCTURE 尺寸 DIMENSIONS L L W T 英制表示 British expression WB WB 型号 Type 尺寸 Dimensions (mm) 公制表示 Metric expression L W T WB 0402 1005 1.00±0.05 0.50±0.05 0.50±0.05 0.25±0.10 0603 1608 1.60±0.10 0.80±0.10 0.80±0.10 0.30±0.10 0805 2012 2.00±0.20 1.25±0.20 1206 3216 3.20±0.30 1.60±0.30 0.80±0.20 1.00±0.20 1.25±0.20 0.80±0.20 1.00±0.20 1.25±0.20 1.60±0.30 0.50±0.20 0.60±0.30 1210 3225 3.20±0.30 2.50±0.30 2.80 0.80±0.30 1808 4520 4.50±0.40 2.00±0.20 2.20 0.80±0.30 1812 4532 4.50±0.40 3.20±0.30 3.50 0.80±0.30 2220 5750 5.70±0.40 5.00±0.40 3.50 1.00±0.40 2225 5763 5.70±0.50 6.30±0.50 6.20 1.00±0.40 备注 : 可根据客户的特殊要求设计符合客户需求的产品 Note:We can design according to customer special requirements 结构 STRUCTURE T W 1 2 3 L 4 5 序号 NO 1 2 3 4 5 名称 Name 陶瓷介质 Ceramic dielectric 内电极 Inner electrode 外电极 Substrate electrode 镍层 Nickel Layer 锡层 Tin Layer 第 2 页共 13 页
三 型号规格表示方法 HOW TO ORDER 0603 P 473 K 500 N T 1 2 3 4 5 6 7 说明 NOTES: 1 尺寸 DIMENSIONS 单位 (unit):inch/ mm 尺寸规格 Size Code 0402 0603 0805 1206 1210 1808 1812 2220 2225 长 宽 (L W) inch 0.04 0.02 0.06 0.03 0.08 0.05 0.12 0.06 0.12 0.10 0.18 0.08 0.18 0.12 0.22 0.20 0.22 0.25 长 宽 (L W) mm 1.00 0.50 1.60 0.80 2.00 1.25 3.20 1.60 3.20 2.50 4.50 2.00 4.50 3.20 5.70 5.00 5.70 6.30.2 介质种类 DIELECTRIC STYLE 介质种类 (Dielectric Code) P 介质材料 (Dielectric) X8R 3 标称容量 NOMINAL CAPACITANCE 表示方式 实际值 (Express Method) (Actual Value) 0R5 0.5 1R0 1.0 102 10 10 2 473 47 10 3 单位 (unit):pf 注 : 头两位数字为有效数字, 第三位数字为 0 的个数 ;R 为小数点 Note: the first two digits are significant; third digit denotes number of zeros; R=decimal point. 第 3 页共 13 页
4 容量误差 CAPACITANCE TOLERANCE 代码 (Code) B C D F G J K M S Z 误差 (Tolerance) ±0.10pF ±0.25pF ±0.5pF ±1.0% ±2.0% ±5.0% ±10% ±20% +50% -20% +80% -20% 备注 :B C D 级误差适用于容量 10pF 的产品. Note:These capacitance tolerance B, C, D are just applicable the capacitance that equals to or less than 10pF. 5 额定电压 RATED VOLTAGE 表示方式 实际值 (Express Method) (Actual Value) 6R3 6.3 500 50 10 0 251 25 10 1 102 10 10 2 单位 (unit):v 注 : 头两位数字为有效数字, 第三位数字为 0 的个数 ; R 为小数点 Note: the first two digits are significant; third digit denotes number of zeros; R=decimal point. 6 端头材料 TERMINAL MATERIAL STYLES 端头类别 (Termination Styles) 三层电镀端头 (Nickel Barrier Termination) 表示方式 (Express Method) N 7 包装方式 PACKAGE STYLES B 散包装 (Bulk Bag) T 编带包装 (Taping Package) 四 温度系数 / 特性 Temperature Coefficient /Characteristics 介质种类 参考温度点 标称温度系数 工作温度范围 Dielectric Reference Temperature Point Temperature Coefficient Operation Temperature Range X8R 20 C ±15% -55 ~150 第 4 页共 14 页
五 电容量范围 Capacitance Range 项目 0402 材料 X8R 电容量工作电压 4V 6.3V 10V 16V 25V 50V 220pF 330pF 470pF 680pF 820pF 1.0nF 1.2nF 1.5nF 1.8nF 2.2nF 3.3nF 3.9nF 4.7nF 第 5 页共 13 页
项目 0603 0805 材料 X8R X8R 电容量工作电压 4V 6.3V 10V 16V 25V 50V 100V 4V 6.3V 10V 16V 25V 50V 100V 220pF 330pF 470pF 680pF 820pF 1000pF 1500pF 2200pF 3300pF 4700pF 5600pF 6800pF 8200pF 10nF 12nF 15nF 22nF 33nF 47nF 68nF 82nF 100nF 120nF 第 6 页共 13 页
项目 1206 1210 材料 X8R X8R 电容量工作电压 4V 6.3V 10V 16V 25V 50V 100V 4V 6.3V 10V 16V 25V 50V 100V 470pF 680pF 820pF 1000pF 1500pF 2200pF 3300pF 4700pF 5600pF 6800pF 8200pF 10nF 12nF 15nF 22nF 33nF 47nF 68nF 82nF 100nF 120nF 150nF 220nF 330nF 470 nf 第 7 页共 13 页
项目 1808 1812 材料 X8R X8R 电容量 工作电压 4V 6.3V 10V 16V 25V 50V 100V 250V 4V 6.3V 10V 16V 25V 50V 100V 250V 1000pF 1500pF 2200pF 3300pF 4700pF 5600pF 6800pF 8200pF 10nF 12nF 15nF 22nF 33nF 47nF 68nF 82nF 100nF 120nF 150nF 220nF 330nF 470nF 560nF 1.0μF 第 8 页共 13 页
项目 2220 2225 材料 X8R X8R 电容量 工作电压 4V 6.3V 10V 16V 25V 50V 100V 250V 4V 6.3V 10V 16V 25V 50V 100V 250V 2200pF 3300pF 4700pF 5600pF 6800pF 8200pF 10nF 12nF 15nF 22nF 33nF 47nF 68nF 82nF 100nF 120nF 150nF 220nF 330nF 470nF 560nF 1.0μF 2.2μF 3.3μF 备注 : 可根据客户的特殊要求设计符合客户需求的产品 Note:We can design according to customer special requirements. 第 9 页共 13 页
六 可靠性测试 Reliability Test 项目 Item 容量 Capacitance 损耗角正切 (DF, tanδ) Dissipation Factor 绝缘电阻 (IR) Insulation Resistance 介质耐电强度 (DWV) Dielectric Withstanding Voltage 技术规格 Technical Specification 测试方法 Test Method and Remarks 测试温度 : 25 ±3 Test Temperature: 25 ±3 应符合指定的误差级别 测试频率 : 1KHZ±10% Should be within the specified tolerance. 测试电压 : 1.0±0.2Vrms Test Frequency: 1KHZ±10% Test Voltage: 1.0±0.2Vrms C 10µF 50V 25V 16V 10V 6.3V 测试频率 : 1KHZ±10% 测试电压 : 1.0±0.2Vrms Test Frequency: 1KHZ±10% Test Voltage: 1.0±0.2Vrms 7.5% C>10µF 2.5% 3.5% 5.0% 5.0% (C<3.3µF) 10.0% (C 3.3µF) C 25 nf, Ri 10000MΩ C>25 nf, Ri C R >100S 不应有介质被击穿或损伤 No breakdown or damage. 测试频率 : 120±24 HZ 测试电压 :0.5±0.1Vrms Test Frequency: 120±24 HZ Test Voltage: 0.5±0.1Vrms 测试电压 : 额定电压测试时间 : 60±5 秒测试湿度 : 75% 测试温度 : 25 ±3 测试充放电电流 : 50mA Measuring Voltage: Rated Voltage Duration: 60±5s Test Humidity: 75% Test Temperature: 25 ±5 Test Current: 50mA 测量电压 :250% 额定电压时间 :1~5 秒充 / 放电电流 : 不应超过 50mA ( 这部分说明不包括中高压 MLCC) Measuring Voltage:250% Rated voltage Duration: 1~5s Charge/ Discharge Current: 50mA max. (This method excludes high-voltage MLCC) 第 10 页共 13 页
项目 Item 可焊性 Solderability 耐焊接热 Resistance to Soldering Heat 抗弯曲强度 Resistance to Flexure of Substrate (Bending Strength) 技术规格 Technical Specification 上锡率应大于 95% 外观 : 无可见损伤. At least 95% of the terminal electrode is covered by new solder. Visual Appearance: No visible damage. ΔC/C -5~+10% DF IR 同初始标准 Same to initial value. 同初始标准 Same to initial value. 外观 : 无可见损伤上锡率 : 95% Appearance:No visible damage.at least 95% of the terminal electrode is covered by new solder. 外观 : 无可见损伤. Appearance: No visible damage. ΔC/C 在 ±10% 范围内 Within ±10% 测试方法 Test Method and Remarks 将电容在 80~120 的温度下预热 10~30 秒. Preheating conditions:80 to 120 ; 10~30s. 有铅焊料 :(Sn/Pb:63/37) 浸锡温度 : 235±5 浸锡时间 : 2±0.5s Solder Temperature: 235±5 Duration: 2±0.5s 无铅焊料 : 浸锡温度 : 245±5 浸锡时间 : 2±0.5s Solder Temperature: 245±5 Duration: 2±0.5s 将电容在 100~200 的温度下预热 10±2 分钟. 浸锡温度 : 265±5 浸锡时间 : 10±1s 然后取出溶剂清洗干净, 在 10 倍以上的显微镜底下观察. 放置时间 :24±2 小时放置条件 : 室温 Preheating conditions: 100 to 200 ; 10±2min. Solder Temperature: 265±5 Duration: 10±1s Clean the capacitor with solvent and examine it with a 10X(min.) microscope. Recovery Time: 24±2h Recovery condition: Room temperature 试验基板 :Al 2 O 3 或 PCB 弯曲深度 :1mm 施压速度 :0.5mm/sec. 单位 :mm 应在弯曲状态下进行测量 T=10 45±2 45±2 Test Board: Al 2 O 3 or PCB Warp: 1mm Speed: 0.5mm/sec. Unit: mm The measurement should be made with the board in the bending position. 第 11 页共 13 页
项目 Item 端头结合强度 Termination Adhesion 温度循环 Temperature Cycle 潮湿试验 Moisture Resistance 技术规格 Technical Specification 外观无可见损伤 No visible damage. ΔC/C: 在 ±10% 范围内 ΔC/C: Within ±10% Δ 在 ±10% 范围内 C/C Within ±10% 2 倍初始标准 DF Not more than twice of initial value. Ri 1000MΩ 或 Ri C R 25S, 取两者之中较小者. IR Ri 1000MΩ or Ri C R 25S, whichever is smaller. 外观 : 无损伤 Appearance: No visible damage. 测试方法 Test Method and Remarks 施加的力 :5N 时间 :10±1S Applied Force: 5N Duration: 10±1S 预处理 : 上限类别温度,1 小时 恢复 :24±1h 初始测量 循环次数 :5 次, 一个循环分以下 4 步 : 阶段 温度 ( ) 时间 ( 分钟 ) 第 1 步 下限温度 (-55) 30 第 2 步 常温 (+20) 2~3 第 3 步 上限温度 (+150) 30 第 4 步 常温 (+20) 2~3 试验后放置 ( 恢复 ) 时间 :24±2h Preheating conditions: up-category temperature, 1h Recovery time: 24±1h Initial Measurement Cycling Times: 5 times, 1 cycle, 4 steps: Step Temperature( ) Time (min.) 1 Low- category temp. (-55) 30 2 Normal temp. (+20) 2~3 3 Up- category temp. (+150) 30 4 Normal temp. (+20) 2~3 Recovery time after test: 24±2h 温度 :40±2 湿度 :90~95%RH 时间 :500 小时 放置条件 : 室温 放置时间 : 48 小时 Temperature:40±2 Humidity:90~95%RH Duration:500h Recovery conditions:room temperature Recovery Time:48h 第 12 页共 13 页
项目 Item 寿命试验 Life Test 中高压产品寿命试验 Middle &high voltage Life Test Δ C/C DF IR 技术规格 Technical Specification 在 ±20% 范围内 Within ±20% 2 倍初始标准 Not more than twice of initial value. Ri 2000MΩ 或 Ri C R 50S, 取两者之中较小者. Ri 2000M Ω or Ri C R 50S, whichever is smaller. 外观 : 无损伤 Visual Appearance: No visible damage. ΔC/C DF IR 在 ±20% 范围内 Within ±20% 2 倍初始标准 Not more than twice of initial value. Ri 2000MΩ 或 Ri C R 50S 取两者之中较小者. Ri 2000M Ω 或 Ri C R 50S whichever is smaller. 外观 : 无损伤 Visual Appearance: No visible damage. 测试方法 Test Method and Remarks 低压产品 (<100V) 电压 :1.5 倍额定工作电压时间 :1000 小时温度 :150 充电电流 : 不应超过 50mA 放置条件 : 室温放置时间 : 48 小时 Low-Voltage(<100V) Applied Voltage: 1.5 Rated Voltage Duration: 1000h Temperature:150 Charge/ Discharge Current: 50mA max. Recovery Conditions: Room Temperature Recovery Time: 48h 中高压产品 : 100V 额定电压 <500V:2 倍工作电压时间 :100 小时充电电流 : 不应超过 50mA 温度 :150 放置条件 : 室温放置时间 : 48 小时, Applied Voltage: 100V Rated Voltage<500V:2 Multiple Duration: 100h Charge/ Discharge Current: 50mA max. Temperature:150 Recovery Conditions: Room Temperature Recovery Time: 48h 注解 : 专门预处理 ( 仅对 2 类电容器 ): 将电容器放在上限类别温度或按详细规范中可能规定的更高温度下经 1h 后, 接着在试验的标准大气条件下恢复 24±1h Note:Pretreatment (only for class2 capacitor) Pretreatment (only for class2 capacitor) is a method to treat the capacitor before measurement. First, place the capacitor in the up-category temperature or other specified higher temperature environment for 1hour. Then recovery the capacitor at standard pressure conditions for 24±1hours 第 13 页共 13 页